High-modulus polyimide film is a kind of resin synthesized by a special formula. The high-modulus polyimide film produced by biaxial stretching process not only has the excellent comprehensive properties of ordinary polyimide film, but also has higher modulus and mechanical strength, lower shrinkage and lower thermal expansion coefficient.
Application: Products can be widely used in high-end electronic industry, high-precision flexible printed circuit board, aerospace and other industries.
| No. | Indicator Name | Unit | TY6052XE50Performance index value | |
| 1 | Appearance | / | The surface should be smooth and clean, and there should be no wrinkles, tears, particles, bubbles, pinholes, foreign impurities and other defects, and the edges should be neat and undamaged. | |
| 2 | Thickness and allowable deviation | um | 5 | |
| ±1 | ||||
| 3 | Tensile strength | Vertical | MPa | ≥200 |
| Horizontal | MPa | ≥200 | ||
| 4 | Elongation at break | Vertical | % | ≥25 |
| Horizontal | % | ≥25 | ||
| 5 | Young’s modulus of elasticity | Vertical | MPa | ≥3500 |
| Horizontal | MPa | ≥3500 | ||
| 6 | Electrical strength | Average value | MV/m | ≥220 |
| Individual values | MV/m | ≥150 | ||
| 7 | Thermal shrinkage
200℃，30min |
Vertical | % | ≤0.15 |
| Horizontal | % | ≤0.15 | ||
| 8 | Surface tension | dyn | ≥52 | |
| 9 | Surface resistivity | Ω | ≥1.0×1010 | |
| 10 | Volumetric resistivity | Ωm | ≥1.0×1014 | |